Method for forming conductors in semiconductor devices

ABSTRACT

A memory device wherein a diode is serially connected to a programmable resistor and is in electrical communication with a buried digit line. An electrically conductive plug is electrically interposed between the digit line and a strapping layer, thereby creating a double metal scheme wherein the strapping layer is a second metal layer overlying metal wordlines. In a method of a first embodiment the strapping material is electrically connected to the digit line through a planar landing pad overlying the conductive plug. An insulative material is sloped to the planar landing pad in order to provide a surface conducive to the formation of the strapping material. In a method of a second embodiment diodes are formed, each having a maximum width equal to f, which is equal to the minimum photolithographic limit of the photolithographic equipment being used, and distanced one from the other along a length of the digit line by a maximum distance equal to f; at least portions of the diodes are masked; at least a portion of an insulative material interposed between two diodes is removed to expose the buried digit line; and the conductive plug is formed in contact with the exposed portion of the buried digit line. After the formation of a programmable resistor in series with the diode a wordline is formed in electrical communication with each of the programmable resistors, and an insulative layer is formed overlying each wordline. Next an insulative spacer layer is deposited and etched to expose the conductive plug. The strapping layer is then formed overlying and in contact with the conductive plug.

[0001] The present invention relates generally to semiconductor devices;and more particularly relates to methods and apparatus for forming digitlines of improved conductivity, such method having particular usefulnessin the fabrication of memory devices, and particularly to memory deviceshaving programmable elements accessible by a diode.

BACKGROUND OF THE INVENTION

[0002] Diode arrays are well known memory storage arrays used insemiconductor memory devices. A selected diode is typically addressedvia digit line and word line selection. A resistance of a programmableresistor in series with the selected diode is controlled to select adesired memory state. In one case the programmable resistor may be anovonic element, such as a chalcogenide material. The internal structureof the chalcogenide is modified to alter its resistance and thereforeits “logic” state. The modification of the structure is ovonic and isdependent on the current which is applied to the element through thediode. It is desirable to reduce stray resistance which may be in serieswith the diode, since by reducing the stray resistance the ovonics canbe more closely controlled with less current, thereby reducing powerrequirements.

SUMMARY OF THE INVENTION

[0003] The invention includes a method and apparatus for forming asemiconductor device wherein a conductive element within the substrateis strapped by another conductive layer above. In one currentlyenvisioned embodiment, another conductive layer will be interposedbetween the substrate and the strapping layer. In one exemplarypreferred implementation, the semiconductor device will be a memorydevice comprising a diode serially connected to a programmable resistor.The diode is in electrical communication with a buried digit line. Anelectrically conductive plug is electrically interposed between thedigit line and a strapping layer, thereby creating a double metalstructure wherein the strapping layer is a second metal layer overlyingmetal wordlines.

[0004] In a method of a first embodiment, the strapping material iselectrically connected to the digit line through a planar landing padoverlying the conductive plug. An insulative material is sloped to theplanar landing pad in order to provide a surface conducive to theformation of the strapping material. Typically a layer of titaniumsilicide is formed on the buried digit line.

[0005] In an exemplary method of forming a second embodiment inaccordance with the present invention, diodes are formed, each having amaximum width equal to f, which may be equal to the minimumphotolithographic limit of the photolithographic equipment being used,and distanced one from the other along a length of the digit line by amaximum distance equal to f; at least portions of the diodes are masked;at least a portion of an insulative material interposed between twodiodes is removed to expose the buried digit line; and the conductiveplug is formed in contact with the exposed portion of the buried digitline. After the formation of a programmable resistor in series with thediode a wordline is formed in electrical communication with each of theprogrammable resistors, and an insulative layer is formed overlying eachwordline. Next all insulative spacer layer is deposited and etched toexpose the conductive plug. The strapping layer is then formed overlyingand in contact with the conductive plug.

[0006] In the second embodiment the width of the diode is equal to f andthe electrically conductive plug is formed within a distance f from asidewall of the diode. An electrically insulative spacer is interposedbetween the plug and the sidewall of the diode. In this embodiment thediode and the plug are made of polycrystalline silicon, although it ispossible to use any conceivable diode structure, for example ametal/semiconductor. In the second embodiment the cathode of the diodeis fabricated in the substrate and the anode is fabricated overlying thesubstrate or vice versa.

[0007] In the typical memory array of the invention the programmableresistor is ovonic and the array is a mesa type structure. The diodesare either planar or container structures.

[0008] The invention provides redundancy since the digit line is aburied component and the strapping layer is an upper component. Thus,even if the metal of the strapping layer breaks, operation of the memorydevice is maintained through the buried digit line. Thus the device hasbetter electromigration reliability, and there is no memory disturbancefrom cell to cell due to the collection of current in the digit line.

[0009] There is space savings when using the structure of the secondembodiment, since the area between cells is no longer just isolationspace but is used instead for contact to the buried digit line, therebyproviding efficient spacing of the cell for high compaction while at thesame time providing good cell to cell isolation.

[0010] By using the double metal scheme of the invention the seriesresistance to the diode is reduced to the diode/programmable resistorstructure. This resistance is decreased even further by providing astrapped conductive plug for every two diodes of the array andphysically interposed therebetween. By using Titanium silicide on theburied digit line in conjunction with the strapped metal layer the bestpacking density is achieved with minimal processing steps. In additionthe titanium silicide is used to minimize the number of connectionsneeded to connect the strapping material and buried digit line.

BRIEF DESCRIPTION OF THE DRAWINGS

[0011]FIG. 1A is a cross sectional view of a substrate in which digitlines have been formed. The cross sectional view of FIG. 1A is takenthrough the width of the digit lines.

[0012]FIG. 1B is a cross sectional view taken through the length of oneof the digit lines shown in FIG. 1A.

[0013]FIGS. 2A and 2B are the cross sectional view shown in FIG. 1Bfollowing depositions of silicon dioxide and polycrystalline silicon.

[0014]FIGS. 3A and 3B are the cross sectional views shown in FIGS. 2Aand 2B, respectively, following a CMP.

[0015]FIG. 4 is the cross sectional view of FIG. 3A following a dopingof the polycrystalline silicon.

[0016]FIG. 5 is the cross sectional view of FIG. 4 following theformation of a contact plug.

[0017]FIG. 6 is a cross sectional view of FIG. 5 following the formationof programmable resistors, word lines and a landing pad.

[0018]FIG. 7 is a cross sectional view of FIG. 6 following the formationand etch of an oxide layer.

[0019]FIG. 8 is a cross sectional view of FIG. 7 following the formationof a strapping layer.

[0020]FIG. 9A is a cross sectional view of a substrate in which digitlines have been formed. The cross sectional view of FIG. 9A is takenthrough the width of the digit lines.

[0021]FIG. 9B is a cross sectional view taken through the length of oneof the digit lines shown in FIG. 9A.

[0022]FIG. 10A is a cross sectional view of a the substrate of FIG. 9Bfollowing the deposition, planarization and masking of an oxide layer.

[0023]FIG. 10B is a top planar view of FIG. 10A.

[0024]FIGS. 11A and 11B are the cross sectional views of FIGS. 9A and9B, respectively, following the formation of polycrystalline siliconregions in the oxide layer of FIGS. 10A and 10B.

[0025]FIG. 12A is the cross sectional view of FIG. 11B following themasking of the polycrystalline silicon regions and the oxide layer andfollowing the etching of the oxide layer in unmasked regions.

[0026]FIG. 12B is a top planar view of FIG. 12A.

[0027]FIG. 13 is a cross sectional view of FIG. 12A following removal ofa masking layer and deposition of a spacer layer.

[0028]FIG. 14 is the cross sectional view of FIG. 13 following theetching of the spacer layer to form spacers adjacent to sidewalls of thepolycrystalline silicon regions.

[0029]FIG. 15 is the cross sectional view of FIG. 14 following adeposition of polycrystalline silicon.

[0030]FIG. 16 is the cross sectional view of FIG. 15 following a CMP.

[0031]FIG. 17A is the cross sectional view of FIG. 16 following theformation of ovonic devices.

[0032]FIG. 17B is the cross sectional view of FIG. 16 following theformation of ovonic devices in a recess of a nitride layer.

[0033]FIGS. 18A and 18B are the cross sectional views of FIGS. 17A and17B, respectively, following the deposition of a conductive layer and anoxide layer and the masking thereof.

[0034]FIGS. 19A and 19B are the cross sectional views of FIGS. 18A and18B, respectively, following removal of exposed portions of theconductive layer and the oxide layer and the mask of FIGS. 18A and 18B.

[0035]FIGS. 20A and 20B are the cross sectional views of FIGS. 19A and19B, respectively, following the deposition of an oxide layer.

[0036]FIGS. 21A and 21B are the cross sectional views of FIG. 20A and20B, respectively, following etching of the oxide layer of FIGS. 20A and20B and the deposition of a strapping layer.

BRIEF DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0037] The invention is described in reference to the exemplaryembodiment of a memory device comprising a diode serially connected to aprogrammable resistor. The diode is in electrical communication with aburied digit line. An electrically conductive plug is electricallyinterposed between the digit line and a strapping layer, therebycreating a “double metal” structure wherein the strapping layer is asecond metal layer overlying metal wordlines.

[0038] In an exemplary memory array the programmable resistor includesan ovonic element and the array is a mesa type structure. Alternately,in a read only memory structure, the programmable resistor may be ananti-fuse device. The diode is either a planar or a container structure,and is used as a setting device to control current to the programmableresistor.

[0039] The method of the first embodiment is discussed relative to FIGS.1A-8. FIG. 1A depicts a p-type substrate 5 which was masked with apattern which defined active areas. Field oxide 6 was then grown toelectrically isolate the active areas, and the mask was removed. Theexposed portions of the substrate 5 are implanted at a dose of 1-9E¹³with a dopant such as phosphorous having an energy of 100-150 KeV tocreate n− regions 7 in the active area of the substrate. Titanium isdeposited and a RTP sinter is performed during which the titanium reactswith the exposed portions of the silicon substrate to form titaniumsilicide 8. Unreacted portions of the titanium are removed with a lowtemperature piranha etch. The titanium silicide regions 8 and the n−region of the substrate 7 form the buried digit lines 10. One of thedigit lines 10 is shown in longitudinal cross-section in FIG. 1B, whileFIG. 1A depicts the entire column pattern in vertical cross-sectionlateral to the digit lines 10.

[0040] The titanium silicide 8 remaining following the piranha etch ismasked (mask not shown) to protect titanium suicide 8 in future contactareas during an etch which removes the titanium silicide 8 in unmaskedregions. The masked is then removed (see FIG. 1B).

[0041]FIGS. 2A and 2B depict the cross sectional view shown in FIG. 1Bfollowing further process steps. In FIG. 2A a relatively thick layer ofsilicon dioxide 15 is deposited to overlie the buried digit lines 10 andthe field oxide 6, which is not shown in this cross section. The silicondioxide 15 is masked with a contact pattern, not shown, definingpolycrystalline silicon plugs and etched to create openings in which thepolycrystalline silicon plugs may be formed. The openings expose thedigit lines 10 in contact regions. After removal of the mask a layer ofpolycrystalline silicon 20 is deposited to fill the openings. Thepolycrystalline silicon 20 is doped. The dopant is selected frommaterials having n− impurities such as phosphorous, antinomy, andarsenic. The dopant may be implanted at 35-150 KeV and a dose of3E¹³-1E¹⁴. The polycrystalline silicon 20 may be deposited in situ anddoped between 1E¹⁶ and 1E¹⁸ atoms/cc or doped after the polycrystallinesilicon 20 is deposited to the same dopant level.

[0042] In an alternate embodiment shown in FIG. 2B the silicon dioxide15 is masked and etched as in FIG. 2A. Following the etch of the silicondioxide 15 the substrate is implanted with a dopant selected frommaterials having p− impurities, such as boron, gallium, and BF₂ to formp− regions 17. The dopants have energies ranging from 50-100 KeV anddosages of 1E¹³-1E¹⁴ atoms/cm² The polycrystalline silicon 20 is thendeposited to fill the openings. In this embodiment the polycrystallinesilicon 20 is implanted or in situ doped with a dopant selected frommaterials having p+ impurities, such as boron, gallium, and BF₂, tocreate a p+ polycrystalline silicon 20. The dopants have energiesranging from 35-50 KeV and dosages of 1E¹⁵ to 5E¹⁵ atoms/cm².

[0043]FIGS. 3A and 3B are the cross sectional views shown in FIGS. 2Aand 2B, respectively, following further process steps. In FIGS. 3A and3B the polycrystalline silicon layer 20 of FIGS. 2A and 2B,respectively, have been planarized, such as through chemical mechanicalplanarization (CMP) to remove portions of the polycrystalline silicon 20overlying the silicon dioxide 15, while at the same time retaining thepolycrystalline silicon 20 in the openings. The CMP is selective to thesilicon dioxide 15. Thus the CMP action stops when the silicon dioxide15 is exposed. In FIG. 3B the p+ polycrystalline silicon 20 and the p−region 17 together form a diode 30 with the digit line 10.

[0044]FIG. 4 is the cross sectional view of FIG. 3A following furtherprocess steps. In FIG. 4 a p+ implant and an activation cycle, whichincludes a rapid thermal process (RTP) cycle and hydrogen cycle, hasbeen performed to create a p+ region 25 at an upper portion of thepolycrystalline silicon 20 of FIG. 3A. During the implant typical p-typedopants, such as Boron, Gallium, and BF₂ are implanted at energy of35-50 KeV and at a dosage of 1E¹⁵ to 5E¹⁵ atoms/cm². The lower portionof the polycrystalline silicon remains n− thereby forming a diode 30vertical to the buried digit line 10. For simplicity the remaining stepsof this embodiment will pertain to diode 30 of FIG. 4 although the samesteps would be applicable if the diode of FIG. 3B were used instead.

[0045] Next the silicon dioxide 15 and diodes 30 are masked (mask notshown), to pattern a contact to the digit line 10. The silicon dioxide15 is etched to form openings (not shown) to expose the digit lines 10,and the resist used for masking is removed.

[0046]FIG. 5 depicts the cross sectional view of FIG. 4 followingfurther process steps. In FIG. 5 a thin layer of titanium and titaniumnitride 35 is deposited along the sidewalls of the openings andoverlying the digit lines 10. Tungsten 40 is deposited to fill theopening and to overly the titanium. The titanium and titanium nitride 35and tungsten 40 are chemically mechanically planarized to expose thesilicon dioxide 15 and form a contact plug 45.

[0047]FIG. 6 depicts the cross sectional view of FIG. 5 followingfurther process steps. In FIG. 6 at least one layer has been deposited,masked and etched to form programmable elements 50 (such as ovonicelements or antifuse elements) overlying each diode 30. In the casewhere an ovonic device is formed several deposition, mask, and etchsteps may be utilized to layer Titanium tungsten, carbon, a firstnitride layer, chalcogenide, and a second nitride layer. Various methodscan be used when forming the ovonic device.

[0048] A first metal layer or stack of approximately 5000 Angstrom isthen deposited to overly the silicon dioxide 15, programmable resistors50 and the contact plug 45. The metal layer is then patterned with amask, not shown, and etched to form wordlines 60 in contact with theprogrammable resistors 50 and a planar landing pad 65 overlying thecontact plug 45. The mask is then removed.

[0049]FIG. 7 is a cross sectional view of FIG. 6 following furtherprocess steps. In FIG. 7 an interlevel dielectric oxide layer 70 isdeposited, chemically mechanically planarized to create a planarsurface, patterned, etched with a wet oxide 7:1 hydrofluoric dip for 15seconds, and dry etched to expose the landing pad 65. The etch of theinvention creates an opening 75 in the oxide 70 having a sloped sidewall80. The direction of the slope is such that the upper portion of theopening has a larger perimeter than that of the lower portion.

[0050]FIG. 8 is a cross sectional view of FIG. 7 following furtherprocess steps. In FIG. 8 a second metal layer or stack, which is wellknown to those skilled in the art, is deposited to overlie the oxide 70and the landing pad 65. The sloped sidewalls 80 are conducive to goodstep coverage during the deposit of the second metal layer.Substantially vertical sidewalls 80 may be employed for tightergeometries. The second metal layer is patterned with a mask and etchedto define and form a strapping layer 85. The mask is then removed.Although this cross section shows one strapping layer 85 in electricalcommunication with one landing pad 65 through one contact plug 45, itshould be noted that a plurality of contact plugs 45 and landing pads 65may be in electrical communication with the digit line 10 and thestrapping layer 85 at a plurality of points to further reduce theresistance in series with the diodes 30. In addition, it should also beremembered that there are a plurality of digit lines formed along othercross sections.

[0051] In a method of a second embodiment diodes are formed, each havinga maximum width equal to f, which is equal to the minimumphotolithographic limit of the photolithographic equipment being used,and distanced one from the other along a length of the digit line by amaximum distance equal to f; at least portions of the diodes are masked;at least a portion of an insulative material interposed between twodiodes is removed to expose the buried digit line; and the conductiveplug is formed in contact with the exposed portion of the buried digitline. After the formation of a programmable resistor in series with thediode a wordline is formed in electrical communication with each of theprogrammable resistors, and an insulative layer is formed overlying eachwordline. Next an insulative spacer layer is deposited and etched toexpose the conductive plug. The strapping layer is then formedself-aligned to the conductive plug.

[0052] In this embodiment the diode and the plug are made ofpolycrystalline silicon, although it is possible that any conceivablediode structure may be used. In the second embodiment the P portion ofthe diode is fabricated in the substrate and the N portion is fabricatedoverlying the substrate.

[0053] In an enhancement of the second embodiment a buried digit line isstrapped at each memory cell to reduce the series resistance therebycreating greater drive. The self alignment feature of the inventionfacilitates a denser array.

[0054] The second embodiment of the invention is depicted in FIGS.9A-21B.

[0055] In FIG. 9A p− digit lines 100 have been formed in an n− substrate105 according to methods known in the art. The present embodiment isshown with LOCOS isolation having field oxide regions 110, but isadapted to trench isolation and modified LOCOS.

[0056]FIG. 9B is a longitudinal cross section through the length of oneof the digit lines 100 shown in lateral cross-section in FIG. 9A.

[0057]FIG. 10A is a cross sectional view of a the substrate of FIG. 9Bfollowing further process steps. In FIG. 10A a conformal silicon dioxidelayer 115 is deposited and planarized, preferably with CMP. The depth ofthe silicon dioxide layer 115 is selected to be greater than the desiredheight of future electrical contact plugs to digit lines 100. Thesilicon dioxide layer 115 is patterned with a photoresist mask 120 todefine the electrical contact plugs. Openings are etched in the exposedportions of the silicon dioxide layer 115 to expose the digit lines 100.By using the method of the invention it is possible to have the minimumwidth of both the masked and unmasked regions along the length of thedigit line equal to f. Thus the method of the invention allows thefabrication of a dense memory array.

[0058]FIG. 10B is a top planar view of the device of FIG. 10A. Since thedigit lines underlie the photoresist mask 120 and silicon dioxide layer115 they are outlined by dashed lines which also define active areas.The field oxide region underlies the silicon dioxide and lies betweentwo digit lines.

[0059]FIGS. 11A and 11B deposit the cross sectional views of FIGS. 9Aand 9B, respectively, following further process steps. In FIGS. 11A and11B the openings have been filled with N+ poly using standard filltechniques. The N+ poly is planarized preferably using CMP. The N+ polyforms contact plugs 125 to the digit lines 100, and the positive N+electrode 130 of the diode is formed from out diffusion of the N typedopant front the N+ poly, thereby avoiding leakage current because thediode behaves as a single crystal diode.

[0060]FIG. 12A depicts the cross sectional view of FIG. 11B followingfurther process steps, and FIG. 12B is a top planar view of the deviceof FIG. 12A. In FIGS. 12A and 12B the contact plugs 125 and silicondioxide 115 shown in FIGS. 11A and 11B are patterned with a mask 135,and the silicon dioxide 115 is etched in unmasked areas to form openings140 to expose the digit lines 100 in the unmasked areas. The mask 135may be misaligned with the contact plugs 125 since the method createsself aligned openings between the contact plugs 125. In one embodimenteach opening eventually allows the strapping layer to be in electricalcontact to the digit line 100 at each memory cell thereby decreasingseries resistance to allow for a higher programming current toadequately set the logic state of a chalcogenide material in an ovonicdevice which will be fabricated overlying each of the contact plugs 125.

[0061] However, the masking may be more selective in order to form feweropenings 140.

[0062]FIG. 12B, as in FIG. 10B, the digit lines have been outlined withdashed lines. In addition portions of contact plugs 125 underlying mask135 are shown with dotted lines.

[0063]FIG. 13 is a cross sectional view of FIG. 12A following furtherprocess steps. In FIG. 13 the mask 135 has been removed and an oxidespacer layer 145 deposited.

[0064]FIG. 14 is a cross sectional view of FIG. 13 following furtherprocess steps. In FIG. 14 the oxide spacer layer has beenanisotropically dry etched to form spacers 150 on the sidewalls of thecontact plug 125. A P+ region 155 is formed in the exposed portion ofthe digit line 100 during a shallow P+ implant, using a dopant from thegroup consisting of BF 2 and at an energy equal to 25-75 KeV and adosage equal to 5E¹⁴-5E¹⁵ atoms/cm², to lower the resistance of a futuremetal interconnect. During the implant it is necessary to protect the n+contact plug 125 with some form of mask (not shown) such as a hand mask.

[0065]FIG. 15 is a cross sectional view of FIG. 14 following furtherprocessing steps. In FIG. 15 a layer of polycrystalline silicon 165 isdeposited.

[0066]FIG. 16 is a cross sectional view of FIG. 15 following furtherprocessing steps. In FIG. 16 the contact plugs 125, spacers 150, andpolycrystalline silicon 165 are CMPed to create a planar surface and toeliminate portions of spacer 150 having non uniform thicknesses. Thespacers 150 following the CMP process provide greater isolationproperties than did the spacers existing before CMP.

[0067] The polycrystalline silicon layer 165 forms a planar landing pad170 following the CMP. A digit line strapping layer may be fabricatedoverlying the landing pad 170 as is explained below. The polycrystallinesilicon 165 is doped P+ using a P+ implant subsequent to theplanarization step.

[0068] In one alternate embodiment which is shown in FIG. 17A thecontact plugs 125 are fabricated to be larger than the photolithographiclimit. FIG. 17A is similar to FIG. 16 except that the contact plugs 125are larger and further processing steps have been performed. An ovonicdevice 175 is fabricated overlying each of the contact plugs 125according to a method of layer fill and etching back according to apattern (not shown) defining the ovonic device 175. The width of theovonic device may be as small as the photolithographic limit therebyallowing more access to the landing pad 170. In this embodiment theovonic device consists of the following layers: tungsten 176, a lowerTiN or TiC_(x)N_(y) layer 177, a nitride layer 182, a chalcogenide layer178, and an upper TiN layer 179. A pore opening 183 is created in thenitride layer 182 and the chalcogenide layer 178 fills the pore opening183. In this method the chalcogenide material is applied usingconventional thin film deposition methods and the other materials of theovonic devices 175 are formed with various methods of layering andetching.

[0069] Typical chalcogenide compositions for these memory cells includeaverage concentrations of Te in the amorphous state well below 70%,typically below about 60% and ranging in general from as low as about23% up to about 56% Te, and most preferably to about 48% to 56% Te.Concentrations of Ge are typically above about 15% and range from a lowof about 17% to about 44% average, remaining generally below 50% Ge,with the remainder of the principal constituent elements in this classbeing Sb. The percentages given are atomic percentages which total 100%of the atoms of the constituent elements. In a particularly preferredembodiment, the chalcogenide compositions for these memory cellscomprise a Te concentration of about 55%, a Ge concentration of about22%, and a Sb concentration of about 22%. This class of materials aretypically characterized as Te_(a)Ge_(b)Sb_(100−(a+b)), where a is equalto or less than about 70% and preferably between about 60% to about 40%,b is above about 15% and less than 50%, preferably between about 17% toabout 44%, and the remainder is Sb.

[0070] An electrically insulative nitride layer 180 is depositedoverlying the ovonic device 190. The nitride layer is patterned in orderto expose at least a portion of the upper surface 181 of the ovonicdevice 175.

[0071]FIG. 17B is a cross sectional view of FIG. 16 following furtherprocessing steps. An ovonic device 190 is fabricated by a second method.When using the second method it is necessary to deposit a nitride layer185 or a combination silicon dioxide layer with an overlying nitridelayer instead of the silicon dioxide layer 115. openings (not shown) areetched partially into the nitride layer 185 or the nitride of thenitride-silicon dioxide combination layer. Recessed ovonic devices 190are then fabricated in the openings overlying the contact plugs 125. Thefabrication comprises a layering, which includes deposition fill andetching back, of the following materials in the sequential order inwhich they are written: tungsten 191, a lower TiC_(x)N_(y) layer 192,chalcogenide layer 193, and an upper TiC_(x)N_(y) layer 194. By usingthis method the chalcogenide material fills the hole without patterning.

[0072] Next wordlines are created. FIGS. 18A and 18B are the crosssectional views of FIGS. 17A and 17B, respectively, following theformation of a conformal conductive layer 200 in electrical contact withthe ovonic devices 175 and 190, respectively. Typically the conductivelayer 200 is a deposit of aluminum, copper, gold, silver, or refractorymetals. An oxide layer 205 is then formed overlying the conductive layer200. The wordlines are patterned with a mask 210 overlying the oxidelayer 205, and exposed portions of the oxide layer 205 are removedduring a first etch, and then exposed portions of the conductive layer200 are removed during a second etch. The portions of the conductivelayer 200 remaining subsequent to the etch form the word lines 215, seeFIGS. 19A and 19B, respectively.

[0073] The mask is then removed, and a conformal oxide layer 220 isdeposited, see FIGS. 20A and 20B, respectively.

[0074] In FIGS. 21A and 21B an oxide spacer 225 is formed toelectrically insulate the wordlines 215 from a future strapping layer.The spacer 225 is formed by anisotropically etching of the oxide layer220. The etch of the oxide layer 220 exposes the landing pads 170 inFIG. 21B. In addition to the oxide layer 220 the nitride layer 180, inFIG. 21A, is etched to expose the landing pads 170 shown in FIG. 21A.

[0075] Further shown in FIGS. 21A and 21B is the strapping layer 230,typically aluminum, copper, or other conductive material, deposited incontact with the landing pad 170. The strapping layer is in electricalcommunication with the digit line 100 through the landing pad 170.Typically the strapping layer 230 is patterned to define desiredinterconnects and then etched according to the pattern. The photoresist(not shown) used for patterning is then removed and the metal isalloyed.

[0076] The invention provides redundancy since the digit line is aburied component and the strapping layer is an upper component. Thus,even if the metal of the strapping layer breaks, operation of the memorydevice is maintained through the buried digit line. Thus the device hasbetter electromigration reliability, and there is no memory disturbancefrom cell to cell due to the collection of current in the digit line.

[0077] There is space savings when using the structure of the secondembodiment, since the area between cells is no longer just isolationspace but is used instead for contact to the buried digit line, therebyproviding efficient spacing of the cell for high compaction while at thesame time providing good cell to cell isolation.

[0078] By using the double metal scheme of the invention the seriesresistance to the diode is reduced to the diode/programmable resistorstructure. This resistance is decreased even further by providing astrapped conductive plug for every two diodes of the array andphysically interposed therebetween. By using titanium suicide on theburied digit line in conjunction with the strapped metal layer the bestpacking density is achieved with minimal processing steps.

[0079] It should be noted that opposite doping may be used throughoutthe described embodiments without departing from the scope of theinvention.

[0080] While the invention is susceptible to various modifications andalternative forms, specific embodiments have been shown by way ofexample in the drawings and have been described in detail herein.However, it should be understood that the invention is not intended tobe limited to the particular forms disclosed. Rather, the invention isto cover all modifications, equivalents, and alternatives falling withinthe spirit and scope of the invention as defined by the appended claims.

What is claimed is:
 1. A memory device, comprising: a digit line formedin a substrate; a memory cell in electrical communication with saiddigit line; a first conductive line in electrical communication withsaid memory cell; and a second conductive line in electricalcommunication with said memory cell.
 2. The memory device of claim 1,wherein said memory cell comprises a chalcogenide element.
 3. The memorydevice of claim 1, wherein said first conductive line comprises a metalelement.
 4. The memory device of claim 1, wherein said second conductiveline comprises a metal element.
 5. The memory device of claim 1, whereinsaid digit line is overlaid with titanium silicide.
 6. The memory deviceof claim 1, wherein said second conductive line is electrically coupledto said digit line at a plurality of contacts.
 7. The memory device ofclaim 1, further comprising an electrical contact plug coupling saiddigit line to said second conductive line.
 8. The memory device of claim11, further comprising a plurality of said electrical contact plugscoupling electrically said digit line to said second conductive line. 9.A memory array, comprising: a plurality of memory cells, each memorycell comprising a programmable resistive element and an access devicecoupled to said resistive element; a digit line in electricalcommunication with said access devices; and a strapping layer inelectrical communication with said digit line at a plurality oflocations.
 10. The memory structure of claim 9, wherein a maximumdistance between each of said ovonic devices is approximately equal to aminimum photolithographic limit.
 11. The memory structure of claim 9,further comprising a first number of access devices coupled to saiddigit line, and a second number of locations at which said strappinglayer is coupled to said digit line, wherein said second number isapproximately one-half said first number.
 12. A memory device,comprising: a first conductive plug having a first type conductivity andhaving a width approximately equal to a minimum photolithographic limit;a second conductive plug having a second type conductivity; and aninsulative spacer interposed between said first and said secondconductive plugs wherein a total width of said second conductive plugand said spacer is approximately no greater than a minimumphotolithographic limit.
 13. A memory device, comprising: two firstconductive plugs having a first type conductivity distanced one from theother by a maximum distance approximately equal to a determineddimension; a second conductive plug having a second type conductivity,said second conductive plus interposed between said two first conductiveplugs; and an insulative spacer interposed between said secondconductive plug and said two first conductive plugs wherein a totalwidth of said second conductive plug and said spacer is no greater thansaid determined dimension.
 14. The memory device of claim 13, whereinsaid determined dimension is representative of a minimum feature sizefor a selected photolithographic process.
 15. A semiconductor device,comprising: a plurality of diodes in electrical communication with asubstrate; a first digit line in electrical communication with saidplurality of diodes; and a strapping layer in electrical communicationwith said first digit line.
 16. The semiconductor device of claim 15,further comprising a plurality of contacts electrically coupled betweensaid first digit line and said strapping layer.
 17. The semiconductordevice of claim 15, further comprising a second digit line physicallybetween said first digit line and said strapping layer.
 18. A method formaking a memory device, comprising the steps of: providing a substratehaving a first conductive line therein; forming a plurality of diodeaccess device memory cells in electrical communication with said firstconductive line; forming a second conductive line, said secondconductive line in electrical communication with one of said memorycells; and forming a third conductive line in electrical communicationwith said first conductive line and said plurality of memory cells. 19.A method for making a memory device, comprising the steps of: providinga substrate having a first conductive line therein; forming a pluralityof memory cells, each said memory cell comprising an elementprogrammable to multiple states of resistance; forming a secondconductive line, said second conductive line in electrical communicationwith one of said memory cells; and creating a third conductive line inelectrical communication with said first conductive line and saidplurality of memory cells.
 20. A method for forming a memory array,comprising the steps of: forming a digit line in a substrate; forming aplurality of memory cells in a first insulative layer, said memory cellsoverlying said digit line and in electrical communication with saiddigit line, each memory cell comprising an element having an alterableresistance, said first insulative layer having an opening therein;forming a contact plug in said opening, said plug in electricalcommunication with said digit line; forming a plurality of firstconductive lines disposed with one of said first conductive linesoverlying and in electrical communication with a selected one of saidmemory cells; and forming a second conductive line in a secondconductive layer, said second conductive line in electricalcommunication with said contact plug.
 21. The method of claim 20,wherein said step of forming said plurality of memory cells furthercomprises the steps of: forming a plurality of diodes in said insulativelayer, said diodes in electrical communication with said digit line; andforming a plurality of programmable devices coupled with each of saiddiodes in electrical communication with a corresponding one of saidelements of alterable resistance.